A Comparative Study on the Influence of Nano and Micro Particles on the Workability and Mechanical Properties of Mortar Supplemented with Fly Ash

In this study, the effects of micro-Al2O3 (MA) and nano-Al2O3 (NA) on the mechanical properties and durability performance of a mortar containing fly ash (FA) were investigated. In the first step, MA and NA were added to the mortar (as a cement replacement) at dosages of 0%, 5%, 10% and 15% by weight. The flowability of the mixture containing NA and MA showed a dosage-dependent behavior, and the addition of MA resulted in a higher flow spread compared with NA. The flow spread increased at 5% (for both NA and MA), and a further increase in the particle content to 10% and 15% decreased the flow spread value. Although the presence of MA and NA contributed to increasing the compressive strength as the particle content increased, the addition of NA resulted in a greater increase in compressive strength (40% increase when adding 15% of NA). The highest splitting tensile strength was obtained when 10% NA was used, and a further increase in the particle content decreased the splitting tensile strength. In the optimization step, the effect of a binder replacement with FA (10, 20 and 30%) in the presence of 10% NA as the optimum level of additive was investigated. Generally, the addition of FA decreased the compressive strength. The highest drop in compressive strength was noticed at early ages, and there was no significant difference in strength development from 14 days to 28 days. A decreasing trend in the splitting tensile strength was observed with the addition of FA content.

Cette oeuvre a été publiée sous la license Creative Commons Attribution 4.0 (CC-BY 4.0). Il est autorisé de partager et adapter l'oeuvre tant que l'auteur est crédité et la license est indiquée (avec le lien ci-dessus). Vous devez aussi indiquer si des changements on été fait vis-à-vis de l'original.